Влияние модифицирования наночастицами SiO2 на кинетику изменений радиационной стойкости оптических свойств микропорошка CaCO3

Статья в сборнике трудов конференции

The study investigated the impact of modifying CaCO3 powder with SiO2 nanoparticles on its radiation resistance of optical properties. The diffuse reflectance spectra of the original and modified pigment were recorded before and after electron irradiation with a fluence of (1-7) ·1016 cm-2 in situ. The main changes in the spectra occurred in the range of 200 to 800 nm. The integral absorption coefficient was calculated, and its change after each irradiation period was determined. The calculations showed that the modified pigment had 2.5 times higher radiation resistance than the unmodified pigment.

Библиографическая запись: Федосов, Д. С. Влияние модифицирования наночастицами SiO2 на кинетику изменений радиационной стойкости оптических свойств микропорошка CaCO3 [Электронный ресурс] / Д. С. Федосов, В. А. Горончко, С. А. Юрьев; научный руководитель М. М. Михайлов // Перспективы развития фундаментальных наук : сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых (Томск, 23-26 апреля 2024 г.) : в 7 т. – Томск : Национальный исследовательский Томский политехнический университет, 2024. – Т. 2. Химия. – С. 271-273.

Конференция:

• Перспективы развития фундаментальных наук
• Россия, Томская область, Томск, 23-26 апреля 2024,
• Международная

Издательство:

Национальный исследовательский Томский политехнический университет

Россия, Томская область, Томск