The Method of Low Temperature ICP Etching InP/InGaAsP Heterostructure in Cl2-based Plasma for Integrated Optics Applications

Статья в журнале

Chlorine processes are widely used for the formation of waveguide structures in InP-based optoelectronics. Traditionally, ICP etching of InP in a Cl2-based plasma requires substrate temperatures in the range of 150–200◦C. This condition is mandatory, since during the etching process low-volatility InClx components are formed and at insufficient temperatures are deposited onto substrate, leading to the formation of defects and further impossibility of the formation of waveguide structures. The need to preheat the substrate limits the application of chlorine processes. This paper presents a method of ICP etching an InP/InGaAsP heterostructure in a Cl2/Ar/N2 gas mixture. A feature of the developed method is the cyclic etching of the heterostructure without preliminary heating. The etching process starts at room temperature. In the optimal etching mode, the angle of inclination of the sidewalls of the waveguides reached 88.8◦ at an etching depth of more than 4.5 µm. At the same time, the surface roughness did not exceed 30 nm. The selectivity of the etching process with respect to the SiNx mask was equal to 9. Using the developed etching method, test integrated waveguide elements were fabricated. The fabricated active integrated waveguide (p-InP epitaxial layers were not removed) with a width of 2 µm demonstrated an optical loss around 11 ± 1.5 dB/cm at 1550 nm. The insertion loss of the developed Y-and MMI-splitters did not exceed 0.8 dB.

Журнал:

  • Micromachines
  • MDPI (Albeuve)
  • Индексируется в Scopus

Библиографическая запись: The Method of Low Temperature ICP Etching InP/InGaAsP Heterostructure in Cl2-based Plasma for Integrated Optics Applications [Electronic resource] / S. lshutkin [et al.] // Micromachines. – 2021. – Iss. 12. – P. 1535. – DOI: 10.3390/mi12121535

Индексируется в:

Год издания:  2021
Страницы:  1 - 18
Язык:  Английский
DOI:  10.3390/mi12121535